Brian Fasteners stocks Aluminium 2014 Bars and Rods, a heat-treatable aluminum alloy with high strength for aerospace, structural, and heavy-industrial use. Its high copper content provides excellent machinability and better mechanical properties, particularly in aerospace-grade tempers. These bars, stocked from our Houston, USA facility, meet ASTM B211 and AMS specifications for traceability and dimensional repeatability. Our 2014 aluminum rods are ideal for intricate engineering applications requiring strength, hardness, and resistance to fatigue. Brian Fasteners provides tailored solutions with swift assistance and international shipping for sophisticated aluminum needs.
Aluminium 2014 is alloyed with ~4.4% copper, 0.8–1.2% manganese, 0.4–0.9% magnesium, and minor silicon and iron. It has tensile strength of 450–540 MPa and yield strength of ~380 MPa (T6 temper) and is among the strongest commercially produced aluminum alloys. It is age hardenable and heat treatable, although with lesser corrosion resistance compared to more pure grades. 2014 machines very well and anodizes well with a deep finish. It is not as well adapted for welding without treatments before and after welding.
| Aluminium Alloy | ASTM B211, B211, B565, B316 5082, AMS 4121 |
| Standard | ASTM, ASME, AMS, GB/T, JIS |
| Aluminium Round Bar Temper | O, H12, H14, H16, H18, H22, H24, H26, H32, H112 |
| Aluminium Bar Form | Aluminium Round, Hex, Flat, Half Round, Oval, Rectangular in Black & Bright Finish |
| Aluminium Round Bar Diameter | 0.1-600mm,etc |
| Aluminium Hexagonal Bar | 0.1-600mm,etc |
| Aluminium Angle Bar Size | 0.5mm*40mm*40mm-20mm*400mm*400mm |
| Aluminium Flat Bar Thickness | 0.1-600mm,etc |
| Aluminium Flat Bar Size | 1-2500mm, etc |
| Aluminium Round Bar Length | 1-12m, Random, Fix & Cut Length or as per clients’ requirement |
| Aluminium Bar | Bright, Polish & Black |
| Aluminium 2014 | Fe | Si | Mg | Mn | Cu | Zn | Ti | Al |
| 0.7 | 0.50 – 1.20 | 0.2 – 0.8 | 0.4 – 1.2 | 3.9 – 5.0 | 0.25 | 0.15 | 93.5 |
| Material | Temper | Diameter (mm) | Tensile Strength min ((N/mm²) | Yield Strength (min) (N/mm²) | Elongation on 5.65 V (min) |
| 2014 Bar | T4 | <20 | 370 | 230 | 11 |
| 2014 Bar | T4 | 20-75 | 390 | 250 | 11 |
| 2014 Bar | T4 | 75-150 | 390 | 250 | 9 |
| 2014 Bar | T4 | 150-200 | 370 | 230 | 8 |
| 2014 Bar | T6510 | 20-75 | 480 | 435 | 7 |
| 2014 Bar | T6510 | 75-150 | 465 | 420 | 7 |
| 2014 Bar | T6510 | 150-200 | 435 | 390 | 7 |
| STANDARD | UNS | WERKSTOFF NR. |
| Aluminium 2014 | A92014 | 3.1255 |
| Size in mm | Average Weight | |
| KG/MTR | KG/FT | |
| 10 | 0.62 | 0.18 |
| 12 | 0.90 | 0.30 |
| 14 | 1.20 | 0.40 |
| 16 | 1.60 | 0.50 |
| 18 | 2.00 | 0.60 |
| 20 | 2.50 | 0.80 |
| 22 | 3.00 | 0.90 |
| 24 | 3.56 | 1.08 |
| 25 | 3.90 | 1.20 |
| 28 | 4.80 | 1.50 |
| 30 | 5.55 | 1.69 |
| 32 | 6.30 | 1.90 |
| 34 | 7.14 | 2.18 |
| 36 | 8.00 | 2.44 |
| 40 | 9.90 | 3.00 |
| 45 | 12.49 | 3.81 |
| 50 | 15.40 | 4.70 |
| 56 | 19.34 | 5.89 |
| 60 | 22.20 | 6.80 |
| 63 | 24.47 | 7.46 |
| 63.5 | 24.86 | 7.58 |
| 65 | 26.05 | 7.94 |
| 70 | 30.20 | 9.20 |
| 73 | 32.86 | 10.00 |
| 75 | 34.72 | 10.58 |
| 78 | 37.51 | 11.43 |
| 80 | 39.50 | 12.00 |
| 83 | 42.47 | 12.95 |
| 85 | 44.55 | 13.58 |
| 90 | 50.00 | 15.20 |
| 92 | 52.19 | 15.91 |
| 93 | 53.39 | 16.27 |
| 95 | 55.65 | 16.95 |
| 100 | 61.66 | 18.79 |
| 105 | 67.98 | 20.72 |
| 110 | 74.60 | 22.74 |
| 115 | 81.64 | 24.88 |
| 125 | 96.34 | 29.36 |
To maintain Aluminium 2014 bars, regularly clean them with mild soap and water to prevent corrosion. Avoid exposure to harsh chemicals and extreme temperatures, and inspect for signs of fatigue or wear.
Aluminium 2014 bars and rods are not ideal for high-temperature applications. While they offer high strength, their performance decreases at elevated temperatures, limiting their suitability for environments above 150°C (302°F).
Aluminium 2014 rods are sized by their diameter, typically ranging from small (e.g., 6 mm) to large (e.g., 100 mm), and are available in various standard or custom lengths.
Aluminium 2014 bars and rods are generally used in aerospace structures, army vehicles, truck frames, and engineering parts that are high in strength and machinability. It is especially appropriate for stressed aircraft components like wing sections, landing gear, and engine mounts. Its resistance to fatigue further qualifies it for drive shafts, gear parts, and forging stock. In the automotive sector, 2014 is utilized for performance suspension systems and brake components. While it needs protection against corrosion, it performs well in harsh load-bearing applications, making it one of the most popular alloys for aerospace-grade structural components.
We provide products that come with both mill test certificates and third-party test certificates, ensuring the highest standards of quality and compliance.
George Metals is a leading manufacturer, supplier, and exporter of high-quality bars, rods, and forgings, catering to various industries in Houston, USA